ABSTRACT

Background: A decline in pH and dissolution of the inorganic content of the dental tissues are followed by exposure of the organic portion of the tooth, which, in dentin, is largely composed of collagen fibres. These unprotected fibres are then degraded by metalloproteinases and cysteine cathepsins, proteolytic enzymes present in dentin. We evaluated the influence of protease inhibitors on the bond strength of a self-etch adhesive system to caries-affected dentin. Eighty permanent third molars were selected for the study. Dentinal caries were induced artificially by the microbial method and the teeth were divided in four groups: G1―application of Clearfil SE Bond adhesive system (CL); G2―2% chlorhexidine (CLX) + CL; G3―sodium bicarbonate (BIC) + CL; G4―BI + CLX + CL. Bond strength was assessed immediately and at six months. During the six months, the specimens were stored in distilled water. Microtensile bond strength testing was performed. On immediate testing, there was no significant difference in bond strength across the control, BIC, and CLX groups. The combination of BIC + CLX, however, led to an immediate, significant reduction in bond strength. After six months, bond strength was reduced in all groups. The highest bond strength was obtained in the control group (P < 0.05). Most fractures were adhesive, both immediately and at six months. We concluded that the cavity pretreatment with 2% CLX or 2% BIC did not have an immediate negative impact on bond strength of the Clearfil SE Bond system. After specimens were stored for six months in water, their bond strength of specimens was reduced in all groups. This reduction was the greatest in the groups exposed to the inhibitors.

Keywords:

Protease Inhibitors, Chlorhexidine, Sodium Bicarbonate, Microtensile Bond, Pretreatment

1. Introduction

The dentinal caries plaque biofilm has a complex structure and produces acids that degrade the inorganic matrix of enamel, dentin, and cementum [1] [2] [3] [4] [5] . A decline in pH and dissolution of the inorganic content of the dental tissues are followed by exposure of the organic portion of the tooth, which, in dentin, is largely composed of collagen fibers. These unprotected fibers are then degraded by metalloproteinases and cysteine cathepsins, proteolytic enzymes present in dentin [6] - [11] . The adhesive system of choice must be hydrophilic enough to interact with the organic content of dentin and hydrophobic enough to interact with the composite resin [12] .

The longevity of adhesive restorations may be compromised by the presence of metalloproteinases. Research has sought to characterize inhibitors of these enzymes. These include 2% chlorhexidine and 17% EDTA [13] [14] . Other inhibitors derived from natural sources have been evaluated for their antiproteolytic activity and fewer side effects as compared with synthetic substances. These include catechins (epigallocatechin gallate, EGCG) extracted from green tea or grapeseed extract [15] [16] . Sodium bicarbonate is a basic substance that can inactivate the cathepsin precursors of endogenous proteases, and could thus act as an indirect metalloproteinase inactivator [17] . Furthermore, it is biocompatible and readily available to dental practitioners.

Self-etching adhesive systems contain acid monomers in their composition. These adhesives systems are capable of forming chemical bonds with the calcium in hydroxyapatite. The stability of these bonds over time is greater than that of conventional adhesive systems, which require phosphoric acid etching prior to application [18] . Self-etch adhesive may be classified on the basis of pH as weak (pH > 2), moderate (1 < pH < 2), or strong (pH < 1) [19] . The weak self-etch adhesives containing the 10-MDP (10-methacryloyloxydecyl dihydrogen phosphate) monomer interact well with calcium in dental tissues increasing the total surface free energy as the surface roughness decreases [20] . MDP ionically bonds to hydroxyapatite through a nanolayer. This characteristic influences the ability of the adhesive system to interact with enamel and dentin [21] [22] . Within this context, the present study sought to assess the influence of protease inhibitors on the bond strength of weak self-etch adhesive systems. The null hypothesis is that there is no significant difference in bond strength of caries-affected dentin when using protease inhibitors.

2. Materials and Methods

The present study was approved by the Research Ethics Committee of PUC- Campinas (protocol number 1.203.078).

2.1. Sample selection

Eighty unerupted permanent third molars were selected at the Dental Clinic of PUC-Campinas. The patients included were male and female and the ages ranged from 20 and 30 years.

Sample size calculation was performed by ANOVA, with a minimum difference between treatment means = 0.23, standard error = 0.25, number of treatments = 4, and statistical power = 0.80. The minimum number of teeth per group was thus calculated as 15.

The inclusion criteria were:unerupted permanent third molars with complete coronal and radicular formation observed in periapical radiography. The permanent third molars included didn’t have done coronal section during extraction and after extraction, the teeth included didn’t have visible cracks or fractures under 10X magnification.

The selected teeth were stored in 0.5% chloramine-T (LabCenter, São Paulo, Brasil) at 37˚C up the begining of research (Marchesi et al., 2014) [20] . The occlusal surface of each specimen was ground down using a double-sided diamond disc (KG Sorensen, Cotia, Brazil) and sanded with silicon carbide papers of descending grit sizes (Norton, Guarulhos, Brazil) in a grinder/polisher (Buehler, Illinois, USA), under water-cooling, to obtain a flat dentin surface. Then, 120-grit and 240-grit sandpaper (Buehler, Illinois, USA) was used to expose the dentin. Finally, 400-grit paper (Buehler, Illinois, USA) was applied for 10 seconds, followed by 600-grit paper (Buehler, Illinois, USA) for 60 seconds, to create a standard smear layer [23] .

2.2. Induction of carious Lesions

The specimens were sealed with epoxy resin (Araldite, São Bernardo do Campo, Brazil) and nail polish (Colorama, São Paulo, Brazil) throughout, except for the dentin surface. The specimens were esterilizated. With the purpose of simulating caries-affected dentin, the teeth were placed in sterile test tubes with brain heart infusion (BHI) broth plus 0.5% yeast extract, 0.5% glucose, and 1% sucrose (all supplies obtained from LabCenter, São Paulo, Brazil). Streptococcus mutans type strain ATCC® 25175™ (Fundação André Tosello, Campinas, Brazil), standardized to 0.5 MacFarland turbidity, was added to the BHI medium. The samples were incubated at 37˚C for 14 days in anaerobic jars with gas-generating envelopes (LabCenter, São Paulo, Brazil) in an atmosphere containing 85% nitrogen (N₂), 10% carbon dioxide (CO₂), and 5% hydrogen (H₂), and stored in a bacteriological incubator. During this 14-day period, BHI broth (LabCenter) was replaced every 24 hours [24] .

2.3. Sample groups

Sterile curettes (SS White, Rio de Janeiro, Brazil) were used to remove infected dentin from all specimens. The criteria used for removal were those suggested by Banerjee and Schwendicke [25] [26] [27] who reported that infected (wet, softened) dentin should be removed, while affected (dry, splintered) dentin should remain in the cavity. The smear layer of the remaining caries-affected dentin was created and standardized manually with 320 grain silicon carbide abrasive papers until hardened dentin, resistant to the touch of sharp exploratory probe, without using pressure, was obtained.

For bond strength testing, experimental groups were randomly divided (http://www.random.org) as follows (n = 20) (Table 1):

Group 1: Clearfil SE Bond adhesive system (Kuraray Noritake Dental; Sakazu, Kurashiki, Okayama, Japan), applied in accordance with manufacturer instructions.

Chemical structures: chlorhexidine (A) and sodium bicarbonate (B).

Group 2: active application of 10 µL 2.0% chlorhexidine (FGM Dentscare LTDA; Joinville, Santa Catarina, Brazil) for 60 seconds, followed by application of Clearfil SE Bond (Kuraray Noritake Dental; Sakazu, Kurashiki, Okayama, Japan) in accordance with manufacturer instructions.

For groups 3 and 4, 200 mg sodium bicarbonate (Biodinâmica, Ibiporã, Brazil) was diluted in 10 mL normal saline to obtain a 2% sodium bicarbonate solution, which was applied to the remaining caries-affected tissue.

Group 3: active application of 10 μL 2.0% sodium bicarbonate (Biodinâmica, Ibiporã, Brazil) for 60 seconds, followed by application of Clearfil SE Bond (Kuraray Noritake Dental; Sakazu, Kurashiki, Okayama, Japan) in accordance with manufacturer instructions.

Group 4: active application of 10 μL 2.0% sodium bicarbonate (Biodinâmica, Ibiporã, Brazil) for 60 seconds, followed by active application of 10 µL 2.0% chlorhexidine (FGM Dentscare LTDA; Joinville, Santa Catarina, Brazil) for 60 seconds, and application of Clearfil SE Bond (Kuraray Noritake Dental; Sakazu, Kurashiki, Okayama, Japan) in accordance with manufacturer instructions.

The application and removal of excess of sodium bicarbonate and chlorhexidine were done with microbrush. The removal excess of protease inhibitors was made until the affected dentin didn’t have moisture.

After application of the adhesive system, a Z350 composite resin build-up (3M ESPE, St. Paul, MN, USA) was made on the dentin surface of each specimen. Each layer of the build-up was approximately 1 mm thick. Layers were oriented parallel to one another and perpendicular to the long axis of the tooth, and were light-cured for 20 seconds. The intensity of the curing light (Gnatus, Ribeirão Preto, Brazil) was 1400 mW/cm², as measured by a radiometer (Curing Light, Brasília, Brazil) at the start of the experiments in each group.

Then, 10 specimens from each group were subjected to immediate microtensile bond strength testing, while the remaining 10 specimens were stored in distilled water for 6 months and then tested [28] .

2.4. Specimen preparation

The teeth were embedded in acrylic and wax (Kota, Cotia, Brazil). Each tooth- adhesive-composite block was sectioned with a diamond disk (Buehler, Illinois, USA), in parallel planes in the buccolingual direction, along the long axis of the tooth. The sections were cut sequentially along the mesiodistal plane to obtain beam-shaped specimens with a cross-sectional area of approximately 1 mm².

Each specimen was visualized under a stereo microscope (Opton, Cotia, Brazil) at 40X magnification to verify that the adhesive interface was perpendicular to the long axis of the specimen.

2.5. Microtensile Bond Strength Testing

Before microtensile bond strength testing, the width and thickness of each specimen were measured with a digital caliper (0.01 mm resolution; Mitutoyo, Suzano, Brazil). The adhesive interface was perpendicular to the long axis of the tensile forces. The assay was performed on a universal testing machine (Instron, São José dos Pinhais, Brazil). Traction was applied to the specimen at a crosshead speed of 0.5 mm/min until fracture occurred. At the time of fracture, the applied load in newtons (N) was recorded and the specimen was examined under a stereo microscope at 40X magnification to ascertain the fracture mode (interface, cohesive in dentin, or cohesive in resin). Only those specimens in which adhesive/mixed-mode fracture at the interface (i.e., debonding) occurred were taken into account for calculation of bond strength. To do so, the fracture load of each specimen was divided by the bond area. Microtensile bond strength tests were performed immediately after specimen preparation and 6 months later.

For statistical analysis, the results of testing were converted from newtons to megapascals (MPa), and each tooth was considered a distinct sampling unit. After testing, all specimens were examined under a stereo microscope (Opton, Cotia, Brazil) at 40X magnification to ascertain the fracture type and percentage as described by Lenzi et al. [28] Fracture mode was scored as follows:

Score 1: Adhesive/mixed-mode fracture;

Score 2: Cohesive fracture in dentin alone;

Score 3: Cohesive fracture in composite resin alone;

Score 4: Premature fracture.

For the analysis of fracture mode, each fractured stick was considered as the sampling unit.

2.6. Statistical analysis

The results were analyzed in the Biostat 4.0 program. D’Agostino’s test for normality revealed that the sample was nonparametric. Therefore, the Kruskal- Wallis test followed by the Student-Newman-Keuls procedure and the Mann- Whitney U test were used for analyses.

3. Results

The longevity of adhesive restorations may be compromised by the presence of metalloproteinases and chlorhexidine was described in literature with a metalloproteinases inhibitor in association with convencional adhesives systems. Sodium bicarbonate is a basic substance that can inactivate the cathepsin precursors of endogenous proteases, and could thus act as an indirect metalloproteinase inactivator. Furthermore, it is biocompatible and readily available to dental practitioners. Within this context, the present study sought to assess the influence of protease inhibitors on the bond strength of weak self-etch adhesive systems.

3.1. Immediate

On immediate testing, there was no significant difference in bond strength between the control and chlorhexidine groups (P > 0.05). Application of sodium bicarbonate was not associated with a significant difference as compared with control, chlorhexidine only, or the combination of bicarbonate and chlorhexidine (P > 0.05). The combination of bicarbonate and chlorhexidine, however, led to a significant reduction in bond strength as compared with the other groups (P < 0.05) (Table 2).

There were no significant differences in fracture mode across groups (P > 0.05) (Table 3).

3.2. Six months

At six months, bonding strength was greatest in the control group, with statistically significant differences in relation to all others (P < 0.05). There was no significant difference in bond strength across the bicarbonate, chlorhexidine, and bicarbonate + chlorhexidine groups (P > 0.05) (Table 4).

There were no significant differences in fracture mode across groups (P > 0.05) (Table 5).

Different letters denote P < 0.05.

Same letter denotes P > 0.05.

Different letters denote P < 0.05.

3.3. Comparative Analysis (immediate vs. Six Months)

Six months after specimen preparation, bond strength was significantly weaker across all groups (P < 0.0001) (Table 6).

4. Discussion

The contemporary restorative dentistry is based on so-called ultraconservative preparations. Removal only of infected dentin tissue, with preservation of caries-affected dentin that is still amenable to structural repair, has been advocated [27] [29] . Within this context, many studies have been conducted to evaluate the behavior of adhesive systems in caries-affected dentin [28] [30] [31] [32] . In the present study, we used the microbial method of artificial caries induction [24] [33] , with bacterial strains and supplemented culture media to simulate the conditions of the oral environment. This method reproduces key characteristics of caries-affected dentin, including differences in substrate color and the presence of two distinct layers within the carious lesion (soft outer layer and harder inner layer) [34] [35] . In addition, the microbial method allows collagen degradation by bacterial esterase [36] . Chemical methods of artificial caries induction do produce demineralization of dentin to an extent capable of simulating the chemical changes that take place in caries-affected tissue, but do not elicit the biological responses observed in the natural process [37] .

Same letter denotes P > 0.05.

Different letters denote P < 0.05.

When using adhesive systems that require phosphoric acid etching, inhibitors have beneficial effects on the durability of bonding to dentin, as they preserve the collagen fibers present largely in the organic dentin portion of the tooth [18] [21] . Conversely, when using self-etch adhesive systems that contain acid monomers, the effects of these inhibitors may not be beneficial [38] . The functional monomers present in self-etch adhesive systems interact with hydroxyapatite to form a chemically stable bond. In the present study, we tested the effect of two protease inhibitors alone and in combination on bonding strength to caries-affected dentin, using the two-step, self-etch Clearfil SE Bond system. The effects of matrix metalloproteinase inhibitors in adhesive interface are preservation of the collagen matrix, the enzymatic chemical bond between metalloproteinase and their inhibitors, or a combination of both mechanisms.

Kim and Shin [39] assessed the anti-Streptococcus mutans activity of one-step and two-step self-etch adhesive systems, with or without light cure, in an agar diffusion experiment. They observed zones of inhibition of bacterial growth around light-cured Clearfil SE Bond adhesive, and attributed this to the presence of residual monomer within the oxygen inhibition layer. Furthermore, they detected the functional acid monomer 10-MDP, which is capable of establishing time-stable chemical bonds with the calcium in hydroxyapatite by encapsulating denuded collagen fibers, trapping proteases in latent form within this collagen matrix [36] [40] which justifies use of the Clearfil SE Bond adhesive system on caries-affected dentin in the present study.

In our sample, pretreatment with 2% chlorhexidine or 2% sodium bicarbonate did not have an immediate negative effect on the bond strength of the Clearfil SE Bond self-etch adhesive system to caries-affected dentin. This corroborates the findings of Sacramento et al. [41] and Mobarak [31] , who found that 2% chlorhexidine was not associated with reductions in immediate bond strength when the Clearfil SE Bond system was applied to carious dentin. This may be explained by the ease with which 10-MDP bonds to residual hydroxyapatite and forms stable calcium salts. In addition, applying the primer and bonding agent in separate steps increases the hydrophobicity of the adhesive layer, thus reducing water flow in the dentin tubules [42] . In a study by Lenzi et al. [43] , chlorhexidine also failed to influence immediate bonding strength to caries-affected dentin in permanent teeth, using a conventional two-step adhesive system. On the other hand, Shafiei et al. [38] tested the influence of pretreatment with 2% chlorhexidine on the bond strength of two self-etch, two-bottle adhesive systems to healthy dentin. The authors found reductions in immediate bond strength of Clearfil SE Bond to healthy dentin pretreated with chlorhexidine, due to cationic bonding of chlorhexidine molecules to the phosphate and calcium in hydroxyapatite. The remaining cations bond to the phosphate anions of 10-MDP molecules. This interaction hinders binding of the 10-MDP functional acid monomer to dentin calcium, thus weakening the bond to dentin.

In the present study, pretreatment of caries-affected dentin with 2% sodium bicarbonate did not interfere with the immediate bond strength of the Clearfil SE Bond system. This may be explained by the lack of any immediate interference of sodium bicarbonate with the effects of the functional acid monomer or with the organic acids present in the primer. Another hypothesis is incorporation of sodium bicarbonate particles into the hybrid layer and smear layer [44] . However, the combination of 2% sodium bicarbonate and 2% chlorhexidine led to an immediate reduction in microtensile bond strength. Possible explanations for this phenomenon include a negative interaction of these two solutions when mixed together, or excessive moisture on the dentin surface caused by consecutive application of the two solutions. The hydrophobic monomer of Clearfil SE Bond adhesive is rendered unable to diffuse into the substrate; instead, globules form in the aqueous environment, preventing infiltration of the bonding agent and its adherence to the caries-affected dentin [44] .

After 6 months, bond strength was diminished in all groups. This disagrees with the findings of Gunaydin et al. [45] . One possible explanation for the increased bond strength in the group not treated with any protease inhibitor is that the 10-MDP functional acid monomer present in Clearfil SE Bond may have bound more strongly to the calcium ions in hydroxyapatite crystals. Application of this weak self-etch adhesive system alone allowed hydroxyapatite to remain around the collagen fibers, thus “fossilizing” proteolytic enzymes. Collagen degradation was mitigated, and the hybrid layer was preserved [40] . In groups pretreated with 2% chlorhexidine, sodium bicarbonate, or a combination of the two, bond strength declined to a greater extent than in the control group. This may be explained by these substances acting as contaminants on the dentin surface, interfering with proper hybridization of dentin tissue with the self-etch adhesive system, which has simultaneous demineralizing and infiltrating action. In addition, specimens were stored in water for 6 months and were thus exposed to hydrolysis of the adhesive interface and collagen degradation in the hybrid layer, which may have led to a breakdown in the adhesive bond [46] .

A high rate of premature fracture was observed in all groups, both immediately after specimen preparation and after 6 months. This may be attributed to the low cohesive strength of caries-affected dentin, and is consistent with the findings of Yoshiyama et al. [47] and Lenzi et al. [36] . In all groups, the predominant fracture mode was adhesive/mixed. This may be explained by the chemical interaction of the adhesive system with the hydroxyapatite present in dentin, forming a bond that is stronger than the dentin or composite resin substrates themselves [48] .

Taking into account the limitations inherent to an in vitro experiment, the present study demonstrated that there is no place for protease inhibitors during adhesive restorations performed with composite resin and the Clearfil SE Bond adhesive system. Further studies in a similar line of research are needed to contribute to the evidence base on this topic.

5. Conclusion

Cavity pretreatment with the protease inhibitors 2% chlorhexidine or sodium bicarbonate did not have an immediate negative impact on bond strength of the Clearfil SE Bond system. At 6 months, however, bond strength was reduced in all groups. This reduction was the greatest in the groups exposed to the inhibitors.

Financial Disclosure

The authors have no financial relationships relevant to this article to disclose.

Conflict of Interest

The authors have no conflicts of interest to disclose.

Cite this paper

Grandizoli, D.R.P. and Pinheiro, S.L. (2018) Influence of Protease Inhibitors on Bond Degradation of Self- Etch Adhesive Systems to Caries-Affected Dentin: An in Vitro Study. Advances in Bio- logical Chemistry, 8, 15-28. https://doi.org/10.4236/abc.2018.81002

References